Screening for Al2O3 failure in MCrAlY APS coatings using short-term oxidation at high temperature

Abstract : The high temperature oxidation behavior of an APS processed γ–β NiCoCrAlY coating was investigated at 1150 °C. Ultrathin freestanding coating specimens ranging from 16 to 240 μm in thickness were tested for short-term oxidation time (< 300 h). Intrinsic chemical failure (InCF) occurred after the full consumption of Al, and resulted in Cr2O3 growth and CrN precipitation at the Al2O3/alloy interface. Mass gain slowed down after InCF, even leading to a mass loss associated with the volatilization of Cr2O3. InCF occurred after [10–20] h and [20–100] h for the ∼ 21 μm and ∼ 31 μm-thick specimens, respectively. Severe metal recession was observed after InCF.
Document type :
Journal articles
Complete list of metadata

https://hal-mines-albi.archives-ouvertes.fr/hal-03196688
Contributor : Imt Mines Albi Ecole Nationale Supérieure Des Mines d'Albi-Carmaux <>
Submitted on : Thursday, April 15, 2021 - 6:41:50 PM
Last modification on : Monday, May 10, 2021 - 4:12:47 PM

File

 Restricted access
To satisfy the distribution rights of the publisher, the document is embargoed until : 2021-09-02

Please log in to resquest access to the document

Identifiers

Citation

Damien Texier, Maxime Ecochard, Thomas Gheno, Daniel Monceau, Mehdi Salem, et al.. Screening for Al2O3 failure in MCrAlY APS coatings using short-term oxidation at high temperature. Corrosion Science, Elsevier, 2021, 184, pp.1-15/109334. ⟨10.1016/j.corsci.2021.109334⟩. ⟨hal-03196688⟩

Share

Metrics

Record views

77