Analysis of AA2XXX/AA7XXX friction stir welds

Résumé

Comparable microstructures and mechanical properties are obtained for the different AA2139-T8/AA7020-T651 joints welded in the range 600–1000 rev. min−1 / 250–550 mm.min−1 as rotation and advance speeds. Joints exhibit tensile properties as good as 77%–79% of the yield strength and 88%–96% of the ultimate tensile strength of the AA7020 base material. Except for the high speed conditions that failed in the nugget, all joint variants failed in the heat affected zone (HAZ), which is also consistent with lower hardness properties. This drop in hardness in the HAZ is produced by reaching and keeping for a short time a critical temperature during welding between 225 and 260 °C. Such a combination of dissimilar alloys offers conservative mechanical properties for a large range of welding parameters suitable for the assembly purpose of high-performance structural components.
Fichier principal
Vignette du fichier
analysis-of-aa2xxx.pdf (14.7 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-02096432 , version 1 (16-04-2019)

Identifiants

Citer

Rémi Bertrand, Hugo Robe, Damien Texier, Yasser Zedan, Eric Feulvarch, et al.. Analysis of AA2XXX/AA7XXX friction stir welds. Journal of Materials Processing Technology, 2019, 271, pp.312-324. ⟨10.1016/j.jmatprotec.2019.03.027⟩. ⟨hal-02096432⟩
176 Consultations
416 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More