Influence of void content on the mechanical properties of carbon/PPS laminates

Abstract : Void content of several carbon fiber/PPS laminates was investigated to assess the impact of porosity level on mechanical properties of thermoplastic materials. Specimens with a [0°/90°] 6 stacking sequence were produced by various autoclave and oven consolidation cycles in order to obtain a void content in the range of 2.0% to 6.0%. Mechanical properties (tensile strength and modulus; flexural strength and modulus, interlaminar shear strength) were measured and results were related to void content. Results show that contrary to tensile strength, flexural and interlaminar shear strength are particulary sensitive to void content. C/PPS tensile and flexural moduli are also weekly affected by void content.
Type de document :
Communication dans un congrès
ECCM17 - 17th European Conference on Composite Materials , Jun 2016, Munich, Germany. Mechanical behavior of amorphous peek in the rubbery state. - ISBN : 978-3-00-053387-7, 2016, 〈http://www.eccm17.org/〉
Liste complète des métadonnées

https://hal-mines-albi.archives-ouvertes.fr/hal-01639004
Contributeur : Abdelmagid El Bakali <>
Soumis le : lundi 20 novembre 2017 - 11:48:28
Dernière modification le : vendredi 13 avril 2018 - 15:36:20

Identifiants

  • HAL Id : hal-01639004, version 1

Collections

Citation

Julien Patou, Gérard Bernhart, Emmanuel De Luycker. Influence of void content on the mechanical properties of carbon/PPS laminates. ECCM17 - 17th European Conference on Composite Materials , Jun 2016, Munich, Germany. Mechanical behavior of amorphous peek in the rubbery state. - ISBN : 978-3-00-053387-7, 2016, 〈http://www.eccm17.org/〉. 〈hal-01639004〉

Partager

Métriques

Consultations de la notice

20